Fresh Properties and Sulfuric Acid Resistance of Sustainable Mortar Using Alkali-Activated GGBSFly Ash Binder

Abstract

In this study, sorptivity, setting time, resistance to sulfuric acid, and compressive strength of mortars that use alkali-activated GGBS and fly ash as binders, were evaluated experimentally. The activation of binders, was achieved at room temperature of 22±20C using combinations of sodium silicates (Na2SiO3) and sodium hydroxide (NaOH) solutions in ratios of 1.5, 2.0, and 2.5. The parameters considered in terms of their effects on fresh and hardened properties include: NaOH molarity, activator ratio Na2SiO3/NaOH, mortar sample age, and relative amount of GGBS/fly ash in binder combination. Sorptivity, change in mass, and compressive strength were determined for mortar samples that were submerged in 10% sulfuric acid solution for 7 days, 28 days, and 90 days. The binder for mortar samples tested at each of the specified ages consisted of 100% GGBS (G100), 75%GGBS+25% fly ash (G75F25), or 50% GGBS + 50% fly ash (G50F50). The binder was activated using Na2SiO3 solution, combined with 10M, 12M, 14M, or 16M NaOH solution. It was found that sorptivity decreases with increase in curing age, for all activator ratios, concentrations, and relative amounts of GGBS/fly ash. Binder consisting of 75%GGBS + 25% fly ash with NaOH concentration of 12M had the lowest sorptivity. Eexposure of alkali-activated GGBS/fly ash mortar samples to sulfate attack did not cause loss in mass nor visible signs of damage/deterioration. All binder combinations experienced increase in compressive strength after curing in 10%sufluric acid solution, with the optimum G75F25 mix achieving a 28-day strength of 80.53 MPa when NaOH molarity is 10M, which increased to 91.06 MPa after 90 days. Variation in concentration of NaOH didn’t cause significant change in the magnitudes of 28-day or 90 day compressive strengths of G50F50. However, despite slow dissolution of fly ash and immersion in 10% sulfuric acid solution, G50F50 developed 28-day compressive strength of 56.23 MPa and 90-day compressive of 86.73 MPa, which qualifies G50F50 as high strength mortar for practical purpose. © 2022 by the authors. Licensee MDPI, Basel, Switzerland.