Enhancing Separation Performance of PA Nanofiltration Membrane Through Polyelectrolyte PSS Interlayer and Surface Modification

Abstract

Thin-film composite (TFC) polyamide (PA) nanofiltration membranes are the state of the art for water purification and reclamation, although a selectivity–permeability trade-off often restricts their development. To mitigate this problem, in this work, a novel three-layer structured nanofiltration (NF) membrane was fabricated consisting of a negatively charged poly (sodium 4-styrenesulfonate) (PSS) interlayer, a high-performance polyethyleneimine (PEI)-based PA separation layer and a PEI-grafted top layer. The PSS interlayer aimed to regulate interfacial polymerization (IP) of PEI with trimesoyl chloride (TMC) and enhance water transport, while PEI-grafting ensured high salt rejections. The relevant characterizations indicated that PEI-grafting endowed the resulting membrane (I-TFC-g) with a positive surface charge and increased the crosslinking degree to achieve much higher rejections for Mg+2 ions through the synergistic effect of Donnan and size-exclusion mechanisms, while the incorporation of the PSS interlayer resulted in an increased pure-water permeability (PWP) value of 7 L m−2 h−1 bar−1 (a value 2.8 times higher compared to the membrane TFC-g without a PSS interlayer). In specific, the I-TFC-g membrane displayed the highest salt rejections of 91% for MgCl2, 92% for MgSO4, 73% for Na2SO4 and 58% for NaCl and a good long-term stability. Overall, this work presents a simple strategy to improve NF performance by simultaneous enhancement of water permeability and salt selectivity.

Keywords: nanofiltration, salt rejection, TFC membrane, water permeability, Chlorite minerals, Composite films, Composite membranes, Grafting (chemical), Nanofiltration membranes, High salts, Poly(ethyleneimine), Poly (sodium 4-styrenesulfonate), Polyamide nanofiltration membranes,Polysodium 4-styrenesulfonate, Salt rejections.